1. How to prolong the life of liner (1)Feed size matching with cavity shape (2)For HP crusher feed should exceed the moving cone separator 300mm For GP crusher feed should exceed frame beam (3)Crusher
How to prolong the life of liner
(1)Feed size matching with cavity shape
(2)For HP crusher feed should exceed the moving cone separator 300mm
For GP crusher feed should exceed frame beam
(3)Crusher avoid intermittent feeding
(4)Control the moisture content of feed materials
(5)Avoid frequent iron overloading
(6)Check the lining in the later stage and replace the liner in good time
(7)The production of new linings at a low load in the preceding period of time when they were put into use, resulting in impact hardening of the linings to prolong their life
(1)The liner must be replaced immediately when it is found that it is deformed (in a depression, a bulge, etc.)
(2)The liner must be replaced immediately when cracks are found
(3)The liner must be replaced immediately when it is loose
If the liner is not replaced in time, the moving cone and the fixed cone body will be damaged.

[ ](/categories/cone-crusher-parts/)[Click to view cone crusher parts introduction](http://en.hnfwe.com/uploads/171226/1-1G226153610239.jpg)
Shuangfeng Qirun Machinery Parts IMP&EXP Co.,Ltd, specializing in the production of domestic and foreign brands of crusher wear spare parts manufacturers, production of domestic brands, Hua Yang, Shan Bao, SBM brands such as crusher wear parts, spare parts, as well as foreign brands, common, Sandvik, TEREX and other import brands crusher spare parts, wear parts, mining quarry companies such as crusher wear parts of choice. We achieve cost-effective localization of imported spare parts, service users at home and abroad. The company can be matched with various brands of hydraulic crusher electric parts, sealing parts, standard parts and other accessories, can meet the needs of one-stop shopping for customers at home and abroad the demand.
Shuangfeng Qirun Machinery Parts IMP&EXP Co.,Ltd has thirty years of production experience, and years of experience in processing export products, products have been exported to the United States, Canada, Australia, Sweden, Finland, Russia, Ukraine and Southeast Asia and other countries and regions. Shuangfeng Qirun Machinery Parts IMP&EXP Co.,Ltd product using the original material, high-quality raw materials, casting and heat treatment process we have a unique thirty years production experience, to ensure complete interchangeability, and original spare parts with high quality and competitive price, provide quality products, quality services for the majority of users.
Shuangfeng Qirun Machinery Parts IMP&EXP Co.,Ltd wearable parts can be customized to map, and if there is no map, the company has professional mapping personnel to help you mapping, after customization
Contact:Sales Director: Eileen Cai ;
Email: sales@qrmech.com;
Mobile telephone: +8618973821771
Trusted by customers in 30+ countries. Standard lead time 15-30 days.
High manganese steel Mn13, Mn13Cr2, Mn18Cr2 and Mn22Cr2, plus high chrome iron (Cr26) for fine crushing. We select the material based on your abrasive and impact conditions - send your working conditions for a recommendation.
Aftermarket parts fit Metso (HP, GP, C, NP series), Sandvik (CH, CS, H, S series), Symons 2FT-7FT, Terex Pegson, Kleemann, McCloskey, Shanbao, SBM, Telsmith, Minyu, Hazemag and more. Any model can be custom made by drawing or sample.
Yes. Send a drawing (PDF, DWG or CAD) or a used sample. We measure, draft and confirm all dimensions with you before production. OEM part numbers are welcome for reference.
Standard lead time is 15-30 days and samples ship in 7-15 days. MOQ is flexible - trial orders from 1 piece are accepted.
ISO 9001 certified factory (Kaixin Certification, CNAS-accredited; certificate valid through June 2028). Every shipment includes a Material Test Report (MTR) with chemical composition and mechanical properties.
Export-standard wooden crates with rust protection. Sea and air freight from Shanghai and Ningbo ports to worldwide destinations.
| Material | Initial Hardness | Best For |
|---|---|---|
| Mn13 (ASTM A128) | HB 200-230 | General crushing with medium impact |
| Mn13Cr2 | HB 210-240 | Standard jaw plates and cone liners |
| Mn18Cr2 | HB 220-250 | High-impact, abrasive feed |
| Mn22Cr2 | HB 230-260 | Severe impact, hard and large rock |
| High Chrome Cr26 | HRC 58-62 | Blow bars, fine crushing of abrasive material |
* High manganese steel work-hardens under impact to 500+ HB at the wearing surface, giving long life in hard-rock crushing.